ALSAN 170 is a PMMA based, fast-curing primer used as a barrier on absorbent substrates in preparation for the later application of Alsan PMMA resins.

Long description, Frame of uses, Advantages

- easy to apply
- fast-curing
- very good adhesion on absorbent substrates
- hydrolysis- and alkali-resistant
- solvent-free

ALSAN 170 is unpigmented.

Composition, technical characteristics, consumption, colors

Colour: ALSAN 170 is unpigmented

• Smooth: 0.4 kg/m²
• Fine‐sandy: 0.5 kg/m²
• Rough: 0.8 kg/m²

Needed tools, installation instructions

Substrate preparation
ALSAN 170 must only be applied to a prepared substrate.
Please refer to the appropriate application guide for information about correct surface preparation.

First stir the tub contents thoroughly. Then add the catalyst whilst stirring at a low speed for 2 minutes.
Make sure that all material on the side and base of the pot is mixed in. At temperatures below 10 °C the
product should be stirred for 4 minutes as the catalyst will take longer to dissolve.

Use the sheepskin roller to apply an even film‐forming coat of primer. Avoid creating puddles of primer. Once the coating has cured, apply a second coat to cover any defects (bubbles, areas not fully coated).

Physico-chemical-thermical performances

2-component, fast-reactive / fast-curing PMMA based (polymethyl methacrylate) primer.

Unit of packaging, dimensions, volume, weight

10 kg metal bucket
ALSAN 170 is supplied without ALSAN 070 catalyst.

Quantity per pallet or box, storage precaution & duration

Store in original sealed packaging in a cool, dry and frost-free place. Avoid warm storage areas (> 30 °C)
even for brief periods, for example on site. Consequently, the products must not be exposed to direct
sunlight or kept in a vehicle. Unopened products have a shelf life of at least 12 months. After opening,
reseal the packaging so it is completely airtight.

EAN and Divalto coding

EAN 13 - 10 kg : 3434550328487